The Shaw process, also known as the Osborn-Shaw process, uses a mixture of refractory aggregate, hydrolyzed ethyl silicate, alcohol, and a gelling agent to create a mold. This slurry mixture is poured into a slightly tapered flask and a reusable pattern (i.e. the item used to create the shape of the mold) is used. The slurry hardens almost immediately to a rubbery state (the consistency of vulcanized rubber). The flask and pattern is then removed. Then a torch is used to ignite the mold, which causes most of the volatiles to burn-off and the formation of ceramic microcrazes (microscopic cracks). These cracks are important, because they allow gases to escape while preventing the metal from flowing through; they also ease thermal expansion and contraction during solidification and shrinkage. After the burn-off, the mold is baked at 1,800 °F (980 °C) to remove any remaining volatiles. Prior to pouring metal, the mold is pre-warmed to control shrinkage.
Read more about this topic: Ceramic Mold Casting
Famous quotes containing the words shaw and/or process:
“I care nothing for all the political parties in the world except as they stand for justice.”
—Anna Howard Shaw (1847–1919)
“My advice to people today is as follows: If you take the game of life seriously, if you take your nervous system seriously, if you take your sense organs seriously, if you take the energy process seriously, you must turn on, tune in, and drop out.”
—Timothy Leary (b. 1920)